Soilworks products are the industry’s top standard due to our insistence on creating high performance soil stabilization and dust control products that stand up to rigorous testing – both in the lab and in the field. Our commitment to quality and performance has led to our involvement and testing in hundreds of real-world situations. The following library of reports, presentations, specifications, approvals and other similar documents provide you, our customer, the transparency and dependable assurance that is expected from Soilworks.
SMI, Inc.
12219 SW 131 Avenue
Miami, Florida 33186-6401 USA
Phone: (305) 971-7047
Fax: (305) 971-7048
Attn: | Fabio Neto Soilworks® LLC 7150 East Camelback Road, Suite 444 Scottsdale, AZ 85251 |
Date:
SMI/REF: |
31-Mar-2021
2101-416 |
Product: | DURASOIL® (received 29-Jan-2021) | ||
Dilution: | As received | Page 1 of 4 |
BOEING SPECIFICATION SUPPORT STANDARD
BSS7432
EVALUATION OF AIRPLANE MAINTENANCE MATERIALS
(Version: Original issue, 28-May-2019 / supersedes Boeing D6-17487)
(Note: Boeing D6-17487 was cancelled and superseded by BSS7432 on 28-May-2019)
Category: Exterior and General Cleaners and Liquid Waxes, Polishes and Polishing Compounds
Sandwich Corrosion Conforms
Test Acrylic Crazing Conforms
Test Paint Softening Test Conforms
Hydrogen Embrittlement Test Conforms
.
Patricia D. Viani, SMI; Inc.
Client: SoilWorks® LLC Date: 31-Mar-2021
Product: DURASOIL SMI/REF: · 2101-416
Dilution: As received
BSS7 432. /Exterior& General. Paoe 2 of 4
Sandwich Corrosion Test: Specimen preparation, tesjting, and interpretation must be in
accordance. with ASTM F1110 using the following materials and with the following
exceptions:
a. Reagents and materials exception:
(1) Clad 7075-T6 aluminum alloy in accordarce with AMS-QQ-A-250/13 (AMS 4049 or AMS-QQ-A-250/13 optional) (2024-T3 Alciad specimens are neither required nor optional.)
(2) Bare 7075-T6 aluminum alloy in accordance with AMS-QQ-A-250/12 (AMS
4045 or AMS-Q-A-250/12 optional) anodized in accordance with BAC 5019
or MIL-A-8625, Type I.
(3) Anodize must be sealed. (2024-T3 nonclad specimens are neither required nor optional
(4) Distilled or deionized water may be used in place of ASTM F1193, Type IV
reagent grade water for control specimens
(5) The filter paper may be Whatman No. 5 or equivalent in place of Whatman GFA glass fiber paper.
b. Procedure exceptions:
(1) The filter paper strips must oe 1 by 3 ipches and must be placed in the
center of the sandwiched specimens.
(2) Each sandwich specimen must be held together with waterproof tape, with
no more than 1 piece of tape (maximum width 0. 75 inch) on each of two
opposite edges.
c. Interpretation of result exceptions:
(1) Leaching or lightening of the chromate sealed anodize coating must not be
cause for rejection.
(2) Deposits or residues from the material being tested that are not products of
corrosion of the test panel surface must ot be cause for rejection.
(3) Special procedure for evaluation of fire extinguishing foams and liquids.
Panels with very light darkening or staining, which have no obvious metal
attack or pitting, may be swabbed (cotton-tipped swabs or cotton gauze)
with a 0.26 mole/liter sulfuric acid solution and re-examined. If the coloration
is substantially removed and there is no evidence of metal attack or pitting,
the condition must not be cause for rejection. (The 0.26 mole/liter sulfuric
acid solution can be prepared by adding 1.5 cc of concentrated sulfuric acid
(SG = 1.84) to 100 cc of distilled or deionized water.
(4) Panels must have a rating of 1 (no more than 5 percent of the surface area
must be corroded) or better in accorqance with ASTM F 1110. The
preferred method of determining the corroded area is by using image
analysis. Other means approved by the purchaser may be substituted.
(5) Any corrosion in excess bf that shown by the control group must be cause
for rejection.
Client: Date: · 31-Mar-2021
Product: DURASOIL · SMI/REF: 2101-416
Dilution: As received
BSS7432 (Exterior & General Page 3 of 4
Sandwich_ Corrosion Test: continued
Bare 7075-T6 (AMS 4045) Anodized per BAC 5019 Type 3 chromate seal) |
Clad 7075-T6 Aluminum (AMS 4049) |
|
Product | 1 | 1 |
Control | 1 | 1 |
Result Conforms
Acrylic Crazing Test:
The material being tested must not craze, crack, or etch acrylic test specimens when tested in accordance with ASTM F 484 using Type C (stretched acrylic plastic in accordance with MIL-P-25690) stressed to an outer fiber stress of 4500 psi.
PRODUCT: No crazing, cracking, or etching
Result Conforms
Paint Softening Test Procedure:
a. Testing must be in accordance with ASTM F502 using the following coating systems.
(1) BMS 10-79, Type II primer applied in accordance with BAC5882 plus
BMS 10-60, Type II enamel in accordance with BAC5845.
(2) BMS 10-79, Type III primer applied in accordance with BAC5882, plus
BMS 10-100 coating in accordance with BAC5797.
b. Three specimens conforming to Section 7.7.a.(1) and three specimens conforming to Section 7.7.a.(2) must be used for each test condition.
c. The material being tested must not produce a decrease in film hardness greater than two pencils, or any discoloration or staining.
NOTE: Slight darkening of the BMS 10-100 surface is acceptable
PRODUCT:
Paint system 1:0 pencil hardness change after 24 hour post-exposure dry time.
No discoloration or staining.
Paint system 2:0 pencil hardness change after 24 hour post-exposure dry time.
No discoloration or staining.
Result Conforms
Client:. SoilWorks® LLC · Date: 31-Mar-2021
Product: DURASOIL SMI/REF: 2101-416
Dilution: As received
BSS87432 (Exterior & General) Page 4 of 4
Hydrogen Embrittlement Test:
Hydrogen Embrittlement testing must be in aocordance with ASTM F 519 using cadmium
plated Type 1a2, Type 1c, or Type 2a specimens. All requirements of ASTM F519 for specimens, preparation, testing, and reporting must apply. Type 1a.2 specimens must
meet the requirements of D6-4307.
Specimens: Type 1c, cadmium plated per MIL-STD-870.
(45% load, 150 hours, notched immersed for the duration, room temp.)
As received:
#1: No failure occurred within 150 hours.
#2: No failure occurred within 150 hours.
#3: No failure occurred within 150 hours.
#4: No failure occurred within 150 hours.
Result Conforms